The semiaustenitic precipitation-hardenable stainless steels remain austenitic on cooling rom a solution heat treatment at about 1950 F. In this form they are readily fabricable. Subsequent treatment at about 1400 or at about 1725 F depletes the austenite of Cr and C to the extent that martensite forms on cooling to room temperature or -100 F, respectively. Final hardening is effected by tempering, or aging, at 750 to 1100 F. The semiaustenitic precipitation-hardenable stainless steels may be obtained as transformed at the mill by cold rolling. In this condition they lack the good formability of solution-heat-treated material. However, the fabricator need only temper them to obtain very high strengths. These steels have a combination of good formability, high strength, and excellent corrosion resistance that is not easily matched by other materials.
Since the combination of tensile properties and toughness that can be obtained with the maraging steels is higher than can be achieved with other steels by simple heat treatments, there is considerable interest in using the maraging steels for critical components such as rocket motor cases, pressure vessels, and aircraft forgings. This report includes information on the tensile, compressive, shear, bearing, dynamic modulus, impact, bend, fatigue, creep, and rupture properties of the 18 per cent nickel maraging steels and on the effect of temperature on these properties. Data for the properties of sheet, bar, and forgings, as well as data illustrating the effect of cold rolling, variation in the heat treatment, and elevated-temperature exposure also are presented. Data on the effect of specimen orientation, which are also included, indicate that the ductility and toughness of specimens designed to evaluate the properties in the short transverse direction are somewhat lower than in the other directions. The high strength and toughness that can be obtained in the 18 per cent nickel maraging steels make them attractive for certain critical applications that require these properties. The fabrication characteristics, weldability, and simple heat treatment are other advantages of these steels. (Author).