Download Free Investigation Of The Use Of Dynamic Modulus As An Indicator Of Hot Mix Asphalt Performance Book in PDF and EPUB Free Download. You can read online Investigation Of The Use Of Dynamic Modulus As An Indicator Of Hot Mix Asphalt Performance and write the review.

This project evaluated the procedures proposed by the Mechanistic-Empirical Pavement Design Guide (MEPDG) to characterize existing hot-mix asphalt (HMA) layers for rehabilitation purposes. Thirty-three cores were extracted from nine sites in Virginia to measure their dynamic moduli in the lab. Falling-weight deflectometer (FWD) testing was performed at the sites because the backcalculated moduli are needed for the Level 1 procedure. The resilient modulus was also measured in the lab because it is needed for the Level 2 procedure. A visual pavement rating was performed based on pavement condition because it is needed for the Level 3 procedure. The selected cores were tested for their bulk densities (Gmb) using the AASHTO T166 procedure and then for their dynamic modulus in accordance with the AASHTO TP62-03 standard test method. Then the cores were broken down and tested for their maximum theoretical specific gravity (Gmm) using the AASHTO T-209 procedure. Finally an ignition test was performed to find the percentage of binder and to reclaim the aggregate for gradation analysis. Volumetric properties were then calculated and used as input for the Witczak dynamic modulus prediction equations to find what the MEPDG calls the undamaged master curve of the HMA layer. The FWD data, resilient modulus data, and pavement rating were used to find the damaged master curve of the HMA layer as suggested for input Levels 1, 2, and 3, respectively. It was found that the resilient modulus data needed for a Level 2 type of analysis do not represent the entire HMA layer thickness, and therefore it was recommended that this analysis should not be performed by VDOT when implementing the design guide. The use of Level 1 data is recommended because FWD testing appears to be the only procedure investigated that can measure the overall condition of the entire HMA layer.
TRB’s National Cooperative Highway Research Program (NCHRP) Report 702: Precision of the Dynamic Modulus and Flow Number Tests Conducted with the Asphalt Mixture Performance Tester describes the development of precision statements for the dynamic modulus and flow number tests conducted with the Asphalt Mixture Performance Tester.
Ohio Department of Transportation has adopted the hot mix asphalt concrete containing polymer modifiers for use in the interstate highway pavement. Among the various reasons cited for the adoption of polymer modifiers are the favorable field experiences by ODOT, extensive literatures reporting enhanced performance, such as rutting resistance, low temperature thermal cracking resistance, and possibly fatigue endurance. However, despite these favorable findings, there are still cases involving premature failure of hot mixtures containing polymer modifiers. Concerns regarding optimum polymer content, compatibility between polymer additives and asphalt cement, proper mixing and compaction procedure remain to be resolved. Furthermore, performance based specifications to ensure production of desirable final asphalt concrete product require additional development. Questions regarding the suitability of Superpave binder testing procedures for the polymer-modified binders need to be clarified.
Explores whether combining the environmental conditioning system with the simple performance test would provide a superior procedure for determining the moisture susceptibility of hot-mix asphalt (HMA).