Published: 1963
Total Pages:
Get eBook
The design and testing procedures of two elevatedtemperature hardness testers are described. One device uses a Rockwell tester with a large vertical capacity and a load range of 15 to 150 kg. The tester is equipped with a 900 deg C heating chamber which maintains an argon atmosphere over the specimen and can be laterally displaced by a cross-feed mechanism to allow repeated hardness readings to be made on the same specimen. The second instrument is a microindentation hardness tester for hardness determinations to a maximum temperature of 1000 deg C in vacuum of 10/sup -4/ to 10/sup -5/ torr. A deadweight loading system with a 136-deg diamond pyramid (Vickers) indenter, capable of delivering static loads between 0.150 and 3 kg, is contained within the vacuum chamber to avoid calibration problems that arise when loads are applied from outside the vacuum system. The microindentation hardness tester allows up to 100 determinations to be made on a single specimen without opening the test chamber. The applicability of the testers is illustrated by elevatedtemperature hardness measurements on several commercial alloys, a group of niobium-vanadium alloys, and by the changes in hardness occurring at the transformation temperatures of iron and steel. Hardness values of Haynes alloy No. 25 were determined at the temperatures of aging and are shown to be different from those obtained with the customary method of investigating age hardening. The testing is currently being used to aid and accelerate the development of alloys with desirable high-temperature properties. (auth).